Zinc-titanium is a modern material produced of the highest purity zinc SHG 99,995% with additions of copper and titanium. Modern technology guaranties very good physical and mechanical properties and allows for wide range of application in building industry.
PRE-AGED GREY – a matt, light grey patina surface created as a result of chemical processes. It is recommended to use pre-aged material on elements such as facades.
PRE-AGED CARBON – a graphite-black surface developed using a complex technological process. The contrasting dark patina provides a distinctive identity whilst harmonising with other building materials such as slate.
Zinc-titanium – Features
|Parameter||PN-EN 988 Requirements||SilesiaZINC Requirements|
|Cooper||0,08 – 1,0%||0,08 – 0,2%|
|Titan||0,06 – 0,2%||0,07 – 0,12%|
|Aluminium||< 0,015%||< 0,015%|
|Standard product dimensional tolerances|
|Thickness (sheets & strips)||±0,03 mm||+0,01/ -0,03 mm|
|Width (sheets & strips)||+2/ -0 mm||+1,0/ -0,0 mm|
|Length||+10/-0 mm||+2,0/-0,0 mm|
|Rectilinearity||< 1,5 mm/m||< 2,0 mm/m|
|Flatness||< 2,0 mm||< 2,0 mm|
|Lower yield point Rp 0,2%||> 100 N/mm²||110 – 150 N/mm²|
|Tensile strength (Rm)||> 150 N/mm²||152 – 180 N/mm²|
|Elongation at break (A50)||> 35%||> 40%|
|Bending test||No cracks at the bend||No cracks at the bend|
|Constant elongation||< 0,1%||< 0,08 %|
|Recrystalization temperature||> 300°C|
|Thermal expansion linear coefficient||0,022 mm/(m*K)|
Creating a protective layer under the influence of atmospheric conditions, that is typical for zinc, causes zinc-titanium has incredibly long-life use and requires practically no maintenance. On initially shining, rolled surface appears patina that is a thin, measuring some micrometers, well adherent protective layer consisting of oxides and basic zinc carbonates.
Zinc-titanium is produced according to EN 988 standard, in two sorts of different surface finish: